Corundum dry shake topping REFLOOR® CT-S600

Refloor® CT-S600 dry shake is a corundum-modified dry single-component cement-based compound for hardening concrete floor surfaces.

Engineering support from estimation to commissioning

Warehouse in Tashkent, Muynakskaya St., 135. Shipping across Uzbekistan and Tajikistan.

Corundum dry shake topping REFLOOR® CT-S600
Corundum dry shake topping REFLOOR® CT-S600
Corundum dry shake topping REFLOOR® CT-S600

Loads

Medium-to-heavy and heavy loads, intensive wheeled traffic

Facilities

Warehouses, production, parking facilities, clean areas

Coating

Seamless, dust-free, easy to clean, chemical-resistant

Description

What makes the system different and what tasks it is typically chosen for.

Refloor® CT-S600 corundum dry shake is a corundum-modified dry single-component cement-based compound for hardening concrete floor surfaces. The material is manufactured in accordance with GOST 31358-2007.

The concrete hardener is intended for finishing the surface of freshly placed concrete floors in production halls, warehouse facilities and parking areas with high load intensity. It reduces dusting and improves surface workability and wear resistance.

Key properties:

  • reduces dusting;
  • has high strength characteristics;
  • provides increased abrasion resistance;
  • compressive strength after 28 days of curing at least 100 MPa;
  • abrasion loss on LKI-3M disc – 0.07 g/m²;
  • does not contain volatile solvents and is odorless;
  • cost efficient.

Material consumption:

  • gray (natural) topping – 3–5 kg/m²;
  • colored topping – 8 kg/m².

The material is a dry, free-flowing fine-grained mixture.
Supplied in 25 kg bags with original printed design.
Pallet weight: 1200 kg (48 bags).

Technical specifications

Material parameters and substrate requirements (TDS/passport).

Strength development period 28 days
Material consumption per 1 m² natural color – 3–5 kg, colored – 8 kg
Layer thickness 2–3 mm
Compressive strength after 28 days min. 105 MPa
Tensile strength after 28 days min. 10 MPa
Bulk density of the mix 1950 kg/m³
Pedestrian traffic after 24 hours
Maximum aggregate size in dry mix 3.2 mm
Light load (up to 200 kg/cm²) after 7 days
Shrinkage max. 0.07%
Service temperature, short-term exposure from −60°C to +300°C
Abrasion loss on LKI-3M disc 0.07 g/cm²
Impact resistance 20.0 kg/mm²

Consumption

Estimated calculation based on area and thickness.

Final figures are confirmed by an engineer based on the actual condition of the substrate.